Effect of different fabrication steps on color and translucency of a CAD-CAM feldspathic ceramic

Camila Sobral Sampaio*, Joyce Belfus, Anai Avila, Carla Cordero, Maria Freitte, Vanina Ferrari, Pablo J. Atria, Gilbert Alex Jorquera Rivera

*Autor correspondiente de este trabajo

Resultado de la investigación: Contribución a una revistaArtículorevisión exhaustiva

Resumen

Objective: To evaluate color differences (ΔE) of different fabrication steps performed on a feldspathic ceramic and relative translucency parameter (RTP) after glazing; and to evaluate their effects on the color parameters: L*, a* and b*. Material and Methods: Computer-aided design/computer-aided manufacturing (CAD-CAM) feldspathic maxillary right central incisor ceramic crowns (Cerec Blocs; 1.4 mm thickness) were fabricated through scanning a model preparation and milling. A total of 20 specimens were used and different parameters were compared with each other for color difference (ΔE): original block, milling, polishing, glazing and try-in cements; RTP was measured after glazing. Color parameters (L*, a*, and b*) were evaluated after each step with a spectrophotometer (Vita Easyshade V) and compared using the CIEDE2000 formula. Statistical analyses were done using one-way ANOVA and post-hoc tests. Results: The highest ΔE value was observed for Original versus Milling group (4.73) and the lowest for Polishing versus Glazing (0.49). RTP after glazing presented a value of 12.01. L*, a*, and b* parameters were different among groups. Milling group was the one that presented more differences compared to the Original block regarding L*, a*, and b* parameters. Conclusions: Different fabrication steps resulted in perceptible color differences within themselves, and L*, a*, and b* parameters changed according to each step. All milling specimens presented unacceptable color differences when compared to the other steps, and milling specimens showed all color parameters (L*, a*, and b*) statistically different compared to the Original block. A high RTP value was observed, demonstrating that, at 1.4 mm thickness, the feldspathic ceramic presented high translucency, showing that opacification of substrate might be necessary. Clinical Significance: Different fabrication steps can greatly affect the optical properties of the feldspathic ceramic restoration studied and cause a relevant impact when compared to the ceramic block itself. Crowns evaluated right after milling presented the highest color differences. In order to obtain optical properties as close as possible to the original feldspathic ceramic block, either polishing or polishing and glazing needs to be performed.

Idioma originalInglés
Páginas (desde-hasta)1038-1044
Número de páginas7
PublicaciónJournal of Esthetic and Restorative Dentistry
Volumen33
N.º7
DOI
EstadoPublicada - oct. 2021

Nota bibliográfica

Publisher Copyright:
© 2021 Wiley Periodicals LLC.

Huella

Profundice en los temas de investigación de 'Effect of different fabrication steps on color and translucency of a CAD-CAM feldspathic ceramic'. En conjunto forman una huella única.

Citar esto