Análisis comparativo in vitro de la resistencia adhesiva al cizallamiento de brackets metálicos adheridos a superficies dentarias tratadas con diferentes agentes blanqueadores

Aim:

To evaluate and compare the effect of three bleaching agents on the shear bond strength of metallic brackets.

Method:

Brackets were cemented on 76 human premolars extracted for orthodontic reasons. 4 groups were evaluated: (0) Control, (1) enamel treated with Carbamide Peroxide 16%, (2) Hydrogen Peroxide 35% and (3) Hydrogen Peroxide 10% “Whitening strips”. All brackets were cemented using Transbond XT adhesive system (3M, Unitek, USA). All samples were thermocycled (5.000 cycles). Shear bond strength was evaluated with a Bisco machine and the amount of adhesive material at the base of the brackets and enamel surface was assessed using the adhesive remnant index (ARI). The statistical analysis included Shapiro-Wilk, Kruskal-Wallis and Mann-Whitney U tests.

Results:

The results of shear bond strength for groups 0, 1, 2, and 3 were 12.64, 11.06, 6.4 and 9.34 MPa respectively, with statistically significant differences between groups (p <0.05). ARI index was significantly different in some groups (p <0.05), indicating cohesive failure for control, adhesive failure for group 2 (p <0.05), adhesive and cohesive failure for groups 1 and 3.

Conclusions:

The 35% hydrogen peroxide office bleaching agent reduces adhesion values in the metal brackets thermocycled 24 hours after bleaching.